Silicone rubber MODRIN MF 5 kg   CATALYST TIXO QUICK 150 g
Silicone rubber MODRIN MF 5 kg   CATALYST TIXO QUICK 150 g

Silicone rubber MODRIN MF 5 kg + CATALYST TIXO QUICK 150 g

MODRIN is a general-purpose mold-making material suitable for casting resins, wax, gypsum, etc. MODRIN is preferred when undercuts are involved and a certain inherent stability of the mold is required.
Tax rate
22 %
Price with VAT:
119,56 €
ADD TO CART

 MODRIN SILICONE RUBBER + CATALYST TIXO QUICK

 

MODRIN is a general-purpose mold-making material suitable for casting resins, wax, gypsum, etc. MODRIN is preferred when undercuts are involved and a certain inherent stability of the mold is required.

 

Modrin cures with 3-5 % of either CATALYST C-88 or CATALYST TIXO QUICK. Curing time for C-88 is 8-12 hours and 2-4 hours with TIXO QUICK. Final hardness is achieved after 24 hours with both catalysts.

 

Catalyst TIXO QUICK speeds up the curing time and is mostly used for vertical application without fine details.

Larger quantities of the catalyst speed up the curing time but render the rubber less flexible and softer.

 

ADVANTAGES

-minimal shrinkage

-finest details reproduction

-flexible and high tear-strength

-high temperature an chemical resistance, max. temperature is 200°C

 

Thickening MODRIN MF by adding TIXO thickener -  for vertical molds (brush-on application)

Add 0,5-1% ofTixo quickener after adding the catalyst. The rubber will thicken in 20 - 30 seconds. Tixo thickener does not have an effect on the curing time of the silicone rubber. 

 

Vertical molds can also be made from MODRIN MF and catalyst TIXO QUICK.

Apply it in several layers. Each application should be thin and wait for 1-2 hours before applying the next layer.

 

PROPERTY TEST METHOD UNIT VALUE
Colour     Blue
Density at 23°C   g/cm³ 1.12
Viscosity at 23°C, afer stirring ISO 3219 mPa.s 25,000

Product data cured with 3% Catalyst C-88

 

PROPERTY TEST METHOD UNIT VALUE
Density at 23°C in water ISO 2781 g/cm³ 1.12
Hardness, Shore A ISO 868   20-25
Tensile strength ISO 867 N/mm² 3,8 ± 0,5
Elongation at break ISO 867 % 15.0 ± 3
Tear strength ASTM D 624 B N/mm² 15.0 ± 3
Linear shrinkage   % 0.6

Cured with 3% of Catalyst C-88, after 4 days at 23°C / 50 % relative humidity

*These figures are intended as a guide and should not be used in preparing specifications.

Related products

    KAMSIL CM 30    30 kg + 3 kg
    Price with VAT:
    785,07 €
    Spray-on Silicone rubber QUICKSIL  750 g + 750 g
    Fast curing spray-on silicone rubber.
    Price with VAT:
    47,58 €
    Silicone rubber K31 1 kg + Catalyst TIXO QUICK 30 g
    White general-purpose mold-making material suitable for casting resins, wax, gypsum, etc. Especially suitable for making specifically coloured molds.
    Price with VAT:
    24,40 €
    FORM-IT white   250 g + 250 g
    FORMIT is a fast curing silicone mold making putty used for making strong, long lasting molds.
    Price with VAT:
    18,30 €
    Cookie - Analitics
    They are used to record the website's obscurity analysis and provide us with data to provide a better user experience.
    Cookie - social
    Cookies required for plug-ins for sharing content from social media sites.
    Cookie - chat
    Cookies allow you to sign up, contact and communicate through the communication plug-in on the page.
    Cookie - marketing
    They target targeted advertising based on past user's activity on other sites.
    What are cookies?
    By visiting and using the site, you consent to the use and recording of cookies.OK Learn more about cookies