MODELIT SPEED fast casting urethane resin 1 kg + 1 kg
Fast curing two-component urethane, used for casting precise model parts, prototypes, tooling boards, casting in electronics; also used as an adhesive...
Tax rate
22 %
Price with VAT:
35,38 €
ADVANTAGES
-fast curing
-simple mixing ratio (1:1)
-casting small and precise parts
-great mechanical properties
-coloration with pigments and pastes
USE
Mix component A to achieve homogeneous colour and consisteny. Mix components A and B at temperatures above 18°C according to the mixing ratio (1:1)
SAFETY PRECAUTIONS
Ensure ventilation, wear protective gloves and goggles.
STORAGE
Shelf life: component A - 6 months ; component B - 12 months , if stored in a dry area in the originally sealed receptable, at temperatures from 15 to 25°C.
Mixing ratio A:B ( by weight)
100 :100
Mixing ratio A:B ( by volume)
at 25˚C 100:84
Mixture colour
white
Density at 23˚C comp. A
1.00
Density at 23˚C comp. B
1.20
Density at 23˚C (mixture)
1.1
Hardness
83 Shore D (at 23˚C)
Impact hardness - Charpy
12 KJ/m2
Elasticity modul
1.100 MPa (at 23˚C)
Tensile strength
48 MPa (at 23˚C)
Curing time, demolding
at 23˚C (thickness 2 mm) >90 minutes
Colour comp. A
white
Colour comp. B
brownish
Elongation at break
4 %
Maximal casting thickness
50 mm
Glass transition temperature ˚C (Tg)
100
Pot life at 25˚C (100 g)
2-3 minutes
Related products
High performance general purpose epoxy laminating resin used in wet-lay or vacuum bagging glass fibre, Kevlar / aramid or carbon fibre laminations.
Price with VAT:
26,58 €
Liquid polymeric foam that hardens into a very rigid foam in a few minutes with an exothermic reaction.
Price with VAT:
219,60 €
Light weight liquid polymer foam which hardens into a rigid foam in a few minutes with an exothermic reaction.
Price with VAT:
35,38 €
Removes air bubbles from the surface of epoxy resins, PUR and similar resins and soap. Can be used with all our epoxy resins (Crystalres, Aquares, Viwood, FastSeal...)
Price with VAT:
6,00 €
Porcelain-like mass for casting into molds.
Price with VAT:
22,33 €
Black, fast-setting paste for filling cracks, knots, voids and other irregularities in wood.
Price with VAT:
14,40 €