Silicone rubber MODRIN MF 1 kg + CATALYST C-88 30 g
MODRIN SILICONE RUBBER + CATALYST C-88
MODRIN is a general-purpose mold-making material suitable for casting resins, wax, gypsum, etc. MODRIN is preferred when undercuts are involved and a certain inherent stability of the mold is required.
Modrin cures with 3-5 % of either CATALYST C-88 or CATALYST TIXO QUICK. Curing time for C-88 is 8-12 hours and 2-4 hours with TIXO QUICK. Final hardness is achieved after 24 hours with both catalysts.
Catalyst TIXO QUICK speeds up the curing time and is mostly used for vertical application without fine details.
Larger quantities of the catalyst speed up the curing time but render the rubber less flexible and softer.
-finest details reproduction
-flexible and high tear-strength
-high temperature an chemical resistance, max. temperature is 200°C
Thickening MODRIN MF by adding TIXO thickener - for vertical molds (brush-on application)
Add 0,5-1% ofTixo quickener after adding the catalyst. The rubber will thicken in 20 - 30 seconds. Tixo thickener does not have an effect on the curing time of the silicone rubber.
Vertical molds can also be made from MODRIN MF and catalyst TIXO QUICK.
Apply it in several layers. Each application should be thin and wait for 1-2 hours before applying the next layer.
|Density at 23°C||g/cm³||1.12|
|Viscosity at 23°C, afer stirring||ISO 3219||mPa.s||25,000|
Product data cured with 3% Catalyst C-88
|Density at 23°C in water||ISO 2781||g/cm³||1.12|
|Hardness, Shore A||ISO 868||20-25|
|Tensile strength||ISO 867||N/mm²||3,8 ± 0,5|
|Elongation at break||ISO 867||%||15.0 ± 3|
|Tear strength||ASTM D 624 B||N/mm²||15.0 ± 3|
Cured with 3% of Catalyst C-88, after 4 days at 23°C / 50 % relative humidity
*These figures are intended as a guide and should not be used in preparing specifications.